FIX-O-FLEX H - adhesive-sealant based on SP polymer (sulfo-polypropylene oxide - SPPO) 600 ml

FIX-O-FLEX H is an adhesive-sealant based on SP polymer (sulfo-polypropylene oxide - SPPO), which has a number of advantages over acrylic, polyurethane and silicone-based sealants. FIX-O-FLEX H sealants are characterized by high chemical resistance, virtually no shrinkage, high adhesive properties, stability at high temperatures, excellent weather resistance and durability. Excellent adhesion to concrete, steel, stainless steel, aluminum, any type of brick, tile, glass, wood, marble, granite, fiberglass, PVC, acrylic, polystyrene and other materials. Technical characteristics: Color: gray endurance, cycles 52000 relative elongation at break at -20°C, % 370; 380 Stickiness temperature, not lower than +75; +76 consistency pasty odor odorless density approx. 1.5 g/cm3 Shore hardness* approx. 25 max. mobility about 25% formation of a surface layer** approximately 2-3 hours complete hardening** approximately 2 mm/24 hours application temperature 5 – 40 ºС (surface temperature) heat resistance -40 to + 80 °C packaging foil tube 600 ml storage 9 months in original packaging in a cool, dry place * Measured 4 weeks after curing at 23°C 50% relative humidity. ** Measured at 23°C and 50% relative humidity. Chemical resistance FK 01-005 Classification: + resistant (no or slight impact) +/– limited resistance (moderate impact) – unstable (severe impact) isopropanol +/– after drying severe changes ethyl acetate +/– after drying severe changes sulfuric acid 96 % – sulfuric acid 10% +/– after drying minor changes gasoline +/– after drying minor changes gas oil +/– after drying minor changes kerosene (Jet A1) +/– after drying minor changes mineral oil 15W40 + brake fluid (DOT 4 ) + o-xylene – m-xylene – toluene – ethylene glycol +/– after drying minor changes methyl ethyl ketone +/– after drying minor changes phosphoric acid 10% +/– after drying minor changes nitric acid 10% – oxalic acid 10% +/ – after drying minor changes citric acid 10% +/– after drying minor changes lactic acid 10% +/– after drying minor changes acetic acid 10% +/– after drying minor changes sodium hydroxide solution 10% +/– after drying minor changes calcium hydroxide solution 20% + ammonium hydroxide 10% + hydrogen peroxide solution 10% + isoparaffin with a high boiling point + Application: To improve adhesion, the surface must be stable, free of resins, oils, and fat. FIX-O-FLEX H can be used without primer on surfaces such as aluminum, galvanized sheets, PVC, PS, Makrolon, etc. If the surface of the seam is porous, it is recommended to pre-treat the walls of the seam chamber with FIX-O-FLEX PRIMER. In the case of highly absorbent surfaces, they must be treated with primer 2 times. For wet surfaces, it is recommended to use HYDROPOX EPG as a primer. Adhesion to difficult-to-bond plastics such as PE or PP (polyolefin) must be checked before starting work. FIX-O-FLEX H sealant must be applied evenly to the surface. It is recommended to use a hand gun. Once a tube of sealant has been opened, it should be used as soon as possible. The curing time of the sealant depends on the humidity and ambient temperature. The time for complete hardening can be reduced by increasing the temperature and humidity. Test Certificates: Study on the interaction of FIX-O-FLEX H sealant with food and commodities (Taunusstein 2000); Testing of FIX-O-FLEX H sealant in accordance with DIN 18 540 (2000); Tensile test on modified bitumen pavements (Leipzig 2003) Resistance of FIX-O-FLEX, FIX-O-FLEX H and FIX-O-FLEX VG to concrete-damaging liquids and sulfuric acid pH 1 (MFPA Leipzig 2003); Water resistance test according to DIN EN 1433 (Leipzig 2004); Chemical resistance test FIX-O-FLEX H in a water pool (Leipzig 2006); Determination of water vapor permeability in accordance with DIN 52 615 (Rostock 2007). Note: FIX-O-FLEX H does not contain any solvents, isocyanates or silicones. Standard precautions for chemical products must be observed. Therefore, before starting work, you need to familiarize yourself with the safety recommendations. FIX-OFLEX H contains aminosilane, which may cause allergic reactions.